UNS N07001 AMS 5586 Welded Tube
UNS N07001 AMS 5586 Welded Tube Manufacturer
According to the UNS N07001 AMS 5586 Welded Tube Manufacturer , Waspaloy (also known as Alloy 685) is a nickel base, age hardenable superalloy with excellent high-temperature strength and good corrosion resistance by combustion products, notably to oxidation, at service temperatures of up to 1200°F (650°C) for critical rotating applications, and up to 1600°F (870°C) for less demanding applications. At temperatures over 1600°F (870°C), intergranular oxidation can occur.
The corrosion resistance is very good even after numerous cycles of elevated temperature exposure, or constant exposure to temperatures of up to 1900°F (1038°C). For the best possible corrosion resistance, solution-treated material is recommended. Waspaloy is also known to behave well in atmospheres in gas turbine engine service and salt spray environments.
Due to these properties, UNS N07001 AMS 5586 Welded Tube Manufacturer deal in Nickel Waspaloy which is to use in gas turbine engine components and aircraft jet engines, such as compressor disks, rotor disks, shafts, spacers, seals, rings, and casings.
UNS N07001 AMS 5586 Welded Tube Manufacturer offers Nickel Waspaloy in 8 sub-type specifications and in multiple shapes/forms:
- AMS 5544 (Plate, Sheet, and Strip)
- AMS 5586 (Tubing)
- AMS 5704 (Forging)
- AMS 5706 (Bar, Forging, and Ring)
- AMS 5707 (Bar, Forging, and Ring)
- AMS 5708 (Bar, Forging, and Ring)
- AMS 5709 (Bar and Forging)
- AMS 5828(Wire)
Chemical Composition of Nickel Waspaloy
Chemical Composition of Nickel Waspaloy (Nominal Composition Alloy 685) Element | min | max |
| Carbon | 0.02 | 0.10 |
| Manganese | — | 0.10 |
| Silicon | — | 0.15 |
| Phosphorus | — | 0.015 |
| Sulfur | — | 0.015 |
| Chromium | 18.00 | 21.00 |
| Cobalt | 12.00 | 15.00 |
| Molybdenum | 3.50 | 5.00 |
| Titanium | 2.75 | 3.25 |
| Aluminum | 1.20 | 1.60 |
| Zirconium | 0.02 | 0.08 |
| Boron | 0.003 | 0.010 |
| Iron | — | 2.00 |
| Copper | — | 0.10 |
| Lead | — | 0.0005 (5 ppm) |
| Bismuth | — | 0.00003 (0.3 ppm) |
| Selenium | — | 0.0003 (3 ppm) |
| Silver | — | 0.0005 (5 ppm) |
| Nickel* | remainder | |
*Not exclusively to the element mentioned, but that one predominates other elements that are used only in minimal quantities.
Fabrication and Working Instructions for Waspaloy
Waspaloy can be hot-worked in the temperature range of 2140-1800°F (1170-980°C), and cold-worked by hydroforming, drawing, spinning, bending, and rolling. That said, this nickel base alloy is difficult to machine and special instructions must be followed.
Physical Constants of Waspaloy (Alloy 685)
| Density | 0.296 lb/in3 |
| 8.19 g/cm3 | |
| Melting Range | 2425-2475°F (1330-1360°C) |
| Coefficient of Thermal Expansion | at 70-200°F (21-93°C) – 6.8 x 10-6 in/in/°F |
| at 70-1000°F (21-583°C) – 7.7 x 10-6 in/in/°F | |
| at 70-2000°F (21-1093°C) – 10.4 x 10-6 in/in/°F | |
| Electrical Resistivity | Solution treated at 1975°F (1080°C) and cooled for 4 hours – 1.24 microhm•m (0.38 microhm•ft) |
| Fully age hardened at 1550°F (845°C), and cooled for 24 hours + reheat to 760°C (1400°F), and cooled for 16 hours – 1.20 microhm•m (0.37 microhm•ft) | |
| Modulus of Elasticity (Dynamic) | at 70°F (21°C) – 30.3 x 103 ksi (211 GPa) |
| at 1000°F (538°C) – 26.7 x 103 ksi (184 GPa) | |
| at 1600°F (871°C) – 22.7 x 103 ksi (157 GPa) | |
| Magnetic Permeability (200 oersteds) | Solution treated + aged – 1.004 |
Minimum Tensile Properties (Room Temp)
| Property | Value |
| Tensile Strength | 175 ksi |
| Yield Strength at 0.2% Offset | 120 ksi |
| Elongation in 4D | 15% |
| Reduction of Area | 18% |
Heat Treating Nickel Waspaloy
Nickel Waspaloy is heat treated in a three-step sequence. There are two different treatments available, both giving different properties to the alloy:
For parts that require optimum tensile properties at room temperature and high-temperature environments:
- Solution treatment – heat at 1825-1895°F (995-1035°C), and then oil quench for 4 hours;
- Stabilization – reheat to 1550°F (845°C), and air cool for 4 hours;
- Age harden – reheat to 1400°F (760°C), and air cool for 16 hours to produce hardness of 33-44 Rockwell C;
Scale may be formed on the alloy during heat treatment in oxidizing atmospheres. However, this doesn’t affect the properties of the alloy and can be removed by acid pickling or mechanically.
AMS 5586 is a specification of Nickel Waspaloy, a nickel-base age-hardenable superalloy with excellent high-temperature strength and good corrosion resistance by combustion products. This superalloy that can be used at temperatures up to 1200°F (650°C) for critical rotating applications, such as rotating parts, and up to 1600°F (870°C) for less demanding applications.
This specification is available as welded and drawn tubing and commonly vacuum-induction and consumable electrode remelted. AMS 5586 is intended for parts that require high-temperature creep and stress rupture properties. The heat treatment is as follows:
- Solution treatment – heat at 1975°F (1080°C), and air cool for 4 hours to produce hardness of 20-25 Rockwell C;
- Stabilization – reheat to 1550°F (845°C), and air cool for 24 hours;
- Age harden – reheat to 1400°F (760°C), and air cool for 16 hours to achieve a hardness of 34-40 Rockwell C;
Please note that scale may be formed on the alloy during heat treatment in oxidizing atmospheres. However, this doesn’t affect the properties of the alloy and can be removed by acid pickling or mechanically.
AMS 5586 can be readily welded only in carefully controlled circumstances, using argon-arc methods and the Waspaloy AMS 5828 filler metal. Welds should be avoided in high-stress environments.
Hot working of AMS 5586 is done at 2140-1800°F (1170-980°C), while hydroforming, drawing, spinning, bending, and rolling can be used for cold working.
Why Choose Us :
- You can get the perfect material according to your requirement at the least possible price.
- We also offer door to door delivery prices. We suggest you to do deal for shipping which will be quite economical.
- The materials we provide are completely verifiable, right from raw material test certificate to the final dimensional statement.(Reports will show on requirement)
- guarantee to give a response within 24hours(usually in the same hour)
- You can get stock alternatives, mill deliveries with minimizing manufacturing time.
- We are fully dedicated to our customers. If it will not possible to meet your requirements after examining all options, we will not mislead you by making false promises which will create good customer relations.
People Also Searched for
| Stainless Steel ASTM A TP 304 Flanges Manufacturer, Stainless Steel ASTM A TP 304L Flanges Manufacturer, Stainless Steel ASTM A TP 304H Flanges Manufacturer, Duplex Steel ASTM 815 Flanges Manufacturer, Duplex Steel UNS S31803 Flanges Manufacturer, Duplex Steel S32750 Flanges Manufacturer, Duplex Steel S32760 Flanges Manufacturer, Duplex Steel S32205 Flanges Manufacturer, Nickel UNS N02200 Flanges Manufacturer, Nickel UNS N02201 Flanges Manufacturer, Alloy 20 Flanges Manufacturer, ASTM A 403 WP TP 304 Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 304L Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 304H Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 316 Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 316L Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 316H Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 316Ti Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 309 Butt Weld Fittings Manufacturer, ASTM A 403 WP TP 904L Butt Weld Fittings Manufacturer, ASTM A 815- UNS S31803 Butt Weld Fittings Manufacturer, ASTM A 815- UNS S32750 Butt Weld Fittings Manufacturer, ASTM A 815- UNS S32760 Butt Weld Fittings Manufacturer, ASTM A 815- UNS S32205 Butt Weld Fittings Manufacturer, ASTM A 234 WPB – WP5 Butt Weld Fittings Manufacturer, ASTM A 234 WPB – WP9 Butt Weld Fittings Manufacturer, ASTM A 234 WPB – WP12 Butt Weld Fittings Manufacturer, ASTM A 234 WPB – WP22 Butt Weld Fittings Manufacturer, ASTM A 234 WPB – WP91 Butt Weld Fittings Manufacturer, ASTM A234 WPB Butt Weld Fittings Manufacturer, A420 WPL3 Butt Weld Fittings Manufacturer, A420 WPL6 Butt Weld Fittings Manufacturer, MSS-SP-75 WPHY 42 Butt Weld Fittings Manufacturer, MSS-SP-75 WPHY 46 Butt Weld Fittings Manufacturer, MSS-SP-75 WPHY 52 Butt Weld Fittings Manufacturer, C71640 Butt Weld Fittings Manufacturer, UNS N02200 Butt Weld Fittings Manufacturer, UNS N02201 Butt Weld Fittings Manufacturer, UNS N04400 Butt Weld Fittings Manufacturer, UNS N05500 Butt Weld Fittings Manufacturer, Alloy 20 Butt Weld Fittings Manufacturer, UNS N06600 Butt Weld Fittings Manufacturer, UNS N06601 Butt Weld Fittings Manufacturer, UNS N06625 Butt Weld Fittings Manufacturer, UNS N08800 Butt Weld Fittings Manufacturer, UNS N08810 Butt Weld Fittings Manufacturer, UNS N10276 Butt Weld Fittings Manufacturer, UNS N06022 Butt Weld Fittings Manufacturer, ASTM A 249 Stainless Steel Welded Manufacturer, ASTM A 268 Stainless Steel Welded Manufacturer, ASTM A 270 Stainless Steel Welded Manufacturer, ASTM A 554 Stainless Steel Welded Manufacturer, ASTM A 1016 Stainless Steel Welded Manufacturer. |
| We Supply ASTM A234 WPB Butt weld Fittings in Andhra Pradesh, Arunachal Pradesh, Assam, Bihar, Chhattisgarh, Goa, Gujarat, Haryana, Himachal Pradesh, Jammu and Kashmir, Jharkhand, Karnataka, Kerala, Madhya Pradesh, Maharashtra, Manipur, Meghalaya, Mizoram, Nagaland, Odisha, Punjab, Rajasthan, Sikkim, Tamil Nadu, Telangana, Tripura, Uttar Pradesh, Uttarakhand, West Bengal, Mumbai, Navi Mumbai, Pune, Nashik, Nagpur, Solapur, Kolhapur, Ambernath, Ahmednagar, Latur, Ahmadabad, Surat, Rajkot, Vadodara, Panaji, Madgaon, Chennai, Kolkata, Hyderabad, Bengaluru, Delhi, New Delhi, Ludhiana, Chandigarh, Raipur, Bhopal, Jamshedpur, Vishakhapatnam, Cochin, Ghaziabad, Noida, Gurugram, Bhillai, Durgapur, Vijaywada, Kanpur etc. |